Guangzhou Tuoshen Surface Treatment Co., Ltd Spray processing It is specialized in painting the surface of plastic shells, but the adhesion of some plastic surface paints is not good, so it is recommended that you choose new materials such as ABS, PP, PE, PVC, etc., and use better plastic paint.

Introduction to process flow
1. Annealing: the plastic is easy to form internal stress during molding, and the stress concentration is easy to crack after coating. Annealing treatment or full face treatment can be used to eliminate stress. Annealing treatment is to heat the ABS plastic molding parts to below the thermal deformation temperature, that is, 60 ℃, and keep them for 2h. Due to mining This process requires a large amount of equipment investment. Therefore, the whole surface treatment technology can be used, that is, the solution that can eliminate the internal stress of the plastic part can be configured to treat the surface of the plastic part for 15-20 minutes at room temperature.

2. Degreasing: The surface of plastic parts is often stained with oil stain, sweat and release agent, which will make the adhesion of paint worse, and the coating will crack, blister and fall off. Oil removal treatment shall be carried out before painting. The plastic parts are usually cleaned with gasoline or alcohol, and then chemical degreasing. After chemical degreasing, the residual lye on the surface of the workpiece should be thoroughly cleaned, and finally cleaned with pure water, dried or dried.

3. De electrification and dedusting: plastic products are insulators, and the surface resistance is generally about 1013 Ω, which is easy to generate static electricity. After electrification, it is easy to absorb fine dust in the air and attach to the surface. Because it is very difficult to remove the electrostatic adsorbed dust by general air blowing method, the effect of simultaneous removal of electrostatic precipitator by high-pressure ionized air flow is better.

4. Spraying: the thickness of plastic coating is 15-20 μ m, which usually requires 2-3 layers of spraying. The second spraying shall be carried out after the first spraying is dried for 15min. Clear paint must also be sprayed on the surface that needs to be bright. The coated parts have little effect on the flame retardancy.

5. Drying: after coating, it can be self dried at room temperature or baked at 60 ℃ for 30min.

Spray processing, Guangzhou spray processing ， Huadu spray processing First, Guangzhou Tuoshen Surface Treatment Co., Ltd. Guangzhou Tuoshen is trustworthy.